Compared to reference parameters in the low power and scan velocity range, which lead to dense and crack-free CM247LC LPBF samples due to in-situ crack healing, high power, high scan velocities and increased laser beam diameters are investigated, to decrease the production time further. By keeping the maximum laser intensity from the reference and the laser power to scan velocity ratio constant, the intensity approach provides an initial estimation for the laser spot size regarding the measured Archimedean density and crack density in the high power and high scan velocity range. The investigated cracks are identified as re-melting cracks. Solidification or hot cracks are not observed, since the crack healing effect for those kinds of cracks still occurs. Furthermore, a melt pool depth range is discovered, where not only solidification cracks can be avoided, but also re-melting cracks, which are resulting from higher laser power inputs. This theory can be proven by further laser spot size optimization, where the melt pool depth comes closer to the mentioned range. The Archimedean density and crack density results, in case of the 600 W power parameter with 2400 mm/s scan velocity and a beam diameter of 164 µm, are close to the one obtained from the reference with 200 W, a scan velocity of 800 mm/s and a laser spot of 90 µm. With the intensity approach and laser beam diameter optimization, the production time can be reduced by 300%. Based on dimensional analysis, a model, which combines the samples density with the crack density through the melt pool depth, is presented. Six main and two additional process and laser parameters are taken into relation. The result from the model and the measured values from experiments are in good agreement. Additionally, the influence of the doubled layer thickness and an increased hatch distance by 50% with varying scan velocities on the Archimedean density and crack density is analysed.