High-energy and long-life O3-type layered cathode material for sodium-ion batteries

doi:10.21203/rs.3.rs-5322440/v1

Download PDF

Article

High-energy and long-life O3-type layered cathode material for sodium-ion batteries

https://doi.org/10.21203/rs.3.rs-5322440/v1

This work is licensed under a CC BY 4.0 License

Version 1

posted

You are reading this latest preprint version

O3-type cathodes for sodium-ion batteries have attracted significant attention owning to their low cost and high energy density. However, their applications are restricted by rapid capacity degradation during long-term cycling, with uneven Na⁺ distribution and microcrack formation being key contributing factors. In this study, a customized reconstruction layer integrating a fast ion conductor NaCaPO₄ coating with gradient Ca²⁺ doping was developed to enhance the surface chemical and mechanical stability of the layered cathodes. The gradient Ca²⁺ doped interphase facilitated uniform phase transformation within the particles, minimized lattice mismatch, ensured even Na⁺ distribution, and mitigated microcrack formation through a pinning effect. Consequently, the optimized cathode delivered excellent rate performance (105.3 mAh g^− 1 at 10 C), long-term cycling stability (81.0% capacity retention after 300 cycles at 0.5 C), and robust reliability under high-voltage conditions and across a wide operating temperature range (− 10 to 50°C). The practical feasibility of a pouch-type Na-ion full cell paired with a hard carbon anode was demonstrated by a high capacity retention of 82.9% after 300 cycles at 1 C. This scalable interface modification strategy can provide valuable insights into the development of advanced oxide cathode materials for sodium-ion batteries.

Physical sciences/Materials science/Materials for energy and catalysis/Batteries

Physical sciences/Energy science and technology/Energy storage/Batteries

Sodium-ion batteries (SIBs), which share a similar electrochemical mechanism with lithium-ion batteries (LIBs), are considered an important supplement to LIB technology due to their low production cost, environmental sustainability, and high safety¹. As a key component that influences the production cost and performance of SIBs, advanced cathode materials with a high energy density and long cycle life must be developed². Among cathode materials, Na layered oxides (Na_xTMO₂, where TM is a transition-metal ion) have emerged as commercially promising candidates owing to their numerous advantages³. Particular attention has been given to O3-type cathodes (Na_xTMO₂, 2/3 < x < 1), which are simple to synthesize, have a high theoretical specific capacity, and are compatible with hard carbon anodes^{4, 5}. However, for O3-type cathodes, achieving good cyclability, especially at high voltages, remains challenging, mainly due to detrimental phase transitions caused by interlayer slip in deep desodiation states, lattice oxygen loss induced by anionic redox reactions, and microcracks formed by anisotropic changes in the lattice parameters^{6, 7}. Furthermore, residual alkali species on the surface react with H₂O and CO₂ in air, leading to surface structure degradation and slurry gelation, which greatly increases transportation and processing costs^{8, 9}.

Conventional modification strategies include anion/cation doping to mitigate adverse phase transitions and enhance the stability of the layered framework structure^{5, 10}, surface coating to improve interfacial stability and prevent electrolyte corrosion¹¹, and multiphase structure construction to reduce irreversible phase transitions^{12, 13}. Increasing research efforts have been directed toward interface modification strategies that integrate gradient doping and surface coating^14–16. For instance, a surface ZrO₂ coating and Zr⁴⁺ doping enhanced the Na storage performance of O3-Na[Mn_1/3Fe_1/3Ni_1/3]O₂ by improving the interfacial air/chemical stability, regulating the anion redox behavior, and optimizing the lattice structure¹⁷. In addition, a Na[Ni_0.4Cu_0.1Mn_0.4Ti_0.1]O₂ cathode modified with a NaMgPO₄ coating, serving as an excellent ion conductor, and Mg²⁺ doping, acting as a stabilizing agent, exhibited an extended high-voltage cycle life¹⁸.

Despite significant progress, previous studies have primarily focused on improvement mechanisms from the perspectives of physical confinement and structural optimization. However, lattice mismatch and internal stress accumulation caused by the uneven distribution of alkali-metal ions within particles are often overlooked¹⁹. The disparity in ion diffusion kinetics between the bulk and surface leads to uneven Na-ion concentration and phase structure, generating surface tensile stress and internal compressive stress, which drive the formation of microcracks—major contributors to mechanical failure^{20, 21}. Shortening the ion diffusion path, improving the ion diffusion kinetics, and stabilizing the layered framework can mitigate the internal stress caused by nonuniform phase transformations and ion diffusion, thereby improving cycling stability²². For example, uniform K-ion doping in the Na layer can enhance the ion reaction kinetics, suppress harmful high-voltage phase transitions, homogenize the Na-ion distribution, and reduce interlayer stress²³. Additionally, the construction of high-entropy and multiphase structures can suppress interlayer slip and enhance Na⁺ migration through structural constraint, thereby preventing structural degradation caused by large ion concentration gradients²⁴. However, homogeneous doping and multiphase structure designs struggle to fundamentally resolve this issue²⁵. Given that the non-uniform distribution of Na-ions predominantly occurs in the near-surface/interface region of the particle, it is proposed to introduce appropriate dopants as pillars into the Na layer at the interface to regulate Na-ion diffusion and phase transition processes.

Building on these concepts, interface reconstruction induced by an epitaxially grown coating is proposed to enhance the Na storage performance of layered oxides. In this study, NaCaPO₄, a fast ion conductor, was systematically investigated as a model coating. In situ spectroscopy and postmortem analysis revealed that coating introduction enhanced the interfacial chemical stability, whereas gradient Ca²⁺ doping mitigated the accumulation of internal stress induced by lattice mismatch through a pinning effect, significantly improving the mechanical stability. Benefiting from this advanced customized interface structure design, the optimized cathode exhibited excellent Na storage performance and air/thermal stability. In particular, satisfactory cycling characteristics were achieved under extreme conditions, such as high voltage (4.5 V vs. Na⁺/Na), high temperature (50°C), and low temperature (− 10°C). The practicality of the optimized cathode was validated in both Na-ion full cells and anode-free cells. This strategy that integrating gradient Ca²⁺ doping and coating is also applicable to other layered oxide cathodes, offering promising prospects for the development of advanced cathode materials for SIBs.

2.1 Formation of interface reconstruction layer

In this study, Na[Ni_0.425Fe_0.15Mn_0.425]O₂ (NFM), a low-cost, high-capacity material with commercial application potential, was used as a model. The Na storage performance was enhanced by bulk doping with Mg and Ti (Na[Ni_0.4Fe_0.1Mn_0.4Mg_0.05Ti_0.05]O₂; NFMMT) to mitigate adverse high-voltage phase transitions and improve the stability of the layered framework structure (Supplementary Fig. 1)^{5, 14}. The powder X-ray diffraction (XRD) results indicate that the Ca₃(PO₄)₂ precoating reacted with surface residual Na species at elevated temperatures (650°C) to form the target NaCaPO₄ (space group: Pnam)-coated NFMMT (NFMMT/NaCaPO₄) cathode (Fig. 1a and Supplementary Fig. 2)²⁶. To demonstrate the enhanced performance of the reconstructed surface, a cathode with homogeneous Ca doping in the Na layer ([Na_0.98Ca_0.01][Ni_0.4Fe_0.1Mn_0.4Mg_0.05Ti_0.05]O₂; NFMMT-Ca doped) was prepared as a control¹⁶.

The chemical composition was verified using inductively coupled plasma optical emission spectrometry (ICP-OES). The calculated normalized ratio is similar to the design value, confirming successful synthesis of the cathode material (Supplementary Table 1). As shown in Supplementary Fig. 3a, all the synthesized cathodes can be indexed to the R3̅m space group, indicating a typical O3-type structure^{5, 11}. The Rietveld refinement results indicate that the doped samples have similar lattice parameters, suggesting that the introduction of low-concentration dopants does not significantly alter the phase structure or interlayer spacing (Supplementary Fig. 4 and Supplementary Table 2)²⁷. According to previous reports, under a sufficient thermodynamic driving force, ion exchange can occur to form a functional gradient-doped interphase²⁸. As Ca–O and Na–O bonds are weaker than TM–O bonds, Na/Ca exchange near the interphase may occur under thermodynamic control and kinetic constraints¹⁶. After high-temperature calcination, a small amount of the P2 phase (space group: P63/mmc) was detected in NFMMT/NaCaPO₄, and the (003) diffraction peak shifted toward a lower angle (Supplementary Fig. 5), indicating a decrease in the Na content of the bulk phase and an expansion of the Na interlayer spacing²⁹. Thus, the coating formation process consumes surface residual Na species and some Na ions from the bulk phase, suggesting that Na/Ca ion exchange occurs at the interface. The corresponding Rietveld-refined XRD pattern reveals lattice parameters of a = 2.967 Å, c = 16.009 Å, and V = 122.069 Å³ for NFMMT/NaCaPO₄, with a structure consisting of 98.6% O3 phase and 1.4% P2-type phase (Fig. 1b). This P2/O3 intergrown structure further enhances the interface stability through biphasic interlocking²⁹. Based on the Williamson–Hall analysis results, NFMMT/NaCaPO₄ exhibits the lowest lattice strain (Supplementary Fig. 3b). Therefore, instead of inducing lattice distortion, the introduction of the interface reconstruction layer promoted the formation of an ordered atomic configuration^{30, 31}. This behavior is attributed to the introduction of surface reconstruction layers that enhance the structural stability of the interface and reduce TM-ion displacement³². The optimal synthesis conditions for the protective layer were determined based on the long-term cycling stability, as excessively high calcination temperatures and thick coating layers can lead to capacity loss and reduced cyclability (Supplementary Figs. 6 and 7)³³. NFMMT/NaCaPO₄ with a 3 wt.% coating was chosen as a representative sample to investigate the structural and electrochemical behavior.

The microstructures of the synthesized cathodes were characterized using scanning electron microscopy (SEM) and dark-field scanning transmission electron microscopy (STEM). As shown in Supplementary Fig. 8, the cathode synthesized via the traditional solid-state method exhibits a typical sheet-like particle morphology, with a diameter of 1–2 µm and a thickness of approximately 100 nm²⁹. In comparison, few particles appear on the surface of NFMMT/NaCaPO₄, indicating the successful introduction of a NaCaPO₄ coating (Fig. 1c). The atomic structure and detailed crystallographic information near the particle edges of the cathode cross section prepared by focused ion beam (FIB) milling were analyzed using STEM and selected area electron diffraction (SAED). As shown in Supplementary Fig. 9, the preferred orientation of the layered oxide leads to the NFMMT cathode having nanosheet crystals with well-defined particle edges. The SAED pattern obtained along the [100] zone axis of an individual particle reveals diffraction spots characteristic of an O3-type structure, indicating high crystallinity and single-crystal properties²². High-resolution TEM (HRTEM) revealed ordered lattice fringes with a spacing of 0.532 nm, corresponding to the (003) crystal plane of the O3 structure, consistent with the XRD results¹⁴.

The NFMMT/NaCaPO₄ exhibits a uniform and continuous surface coating with a thickness of approximately 10 nm, demonstrating the consistency of the wet chemical coating process (Fig. 1f). HRTEM images show that the bulk structure of the modified cathode maintains a layered configuration, whereas the surface has lattice fringes with spacings of 0.266 nm, corresponding to the (031) facets of NaCaPO₄, confirming the successful formation of a surface protective layer (Fig. 1g). Notably, the epitaxially grown NaCaPO₄ is oriented perpendicular to the (003) crystal plane, creating a lattice-anchored interface that can facilitate ion conduction and enhance the air/chemical stability of the layered oxides (Supplementary Fig. 10)¹¹. The relatively bright contrast observed between adjacent TM layers near the interface of the main O3 structure is nearly invisible within the particles (approximately 20 nm) (Fig. 1h). As Na/O atoms are challenging to identify because of their low atomic weights, the pronounced differences in the intensity profile of the Na-layer columns directly indicate the presence of Ca atoms in the Na layer^{34, 35}. Similarly, the intensity line profile reveals strong Ca²⁺ signals near the surface (Fig. 1i). Additionally, the interlayer spacing of the O3-type layered structure near the interface (0.532 nm) is slightly smaller than that in the core region (0.535 nm). This slight lattice contraction is attributed to the enhanced interlayer binding energy resulting from Ca²⁺ intercalation³⁶.

The elemental distributions of the particles were analyzed using TEM and energy-dispersive X-ray spectroscopy (EDS). The elemental mapping image shows that the TM elements are uniformly distributed in NFMMT/NaCaPO₄, whereas signals corresponding to aggregated Ca and P appear near the particle surface, suggesting a heterogeneous surface structure at the particle level (Fig. 1j). TEM-EDS elemental line scanning was used to track changes in the Ni/Fe/Mn and Ca/P concentrations at the particle edges (Fig. 1k). The X-ray intensity of Ni/Fe/Mn decreases after passing through the particles, whereas that of Ca/P increases sharply at the particle boundary. In addition, the distribution of Ca is approximately 10 nm wider than that of P, indicating that the introduction of the NaCaPO₄ protective layer induced gradient Ca doping at the interface²⁸. These results demonstrate the successful synthesis of a reconstruction layer composed of a 10 nm NaCaPO₄ coating and a 10 nm gradient Ca-doped interphase, which enhances the stability of the interface structure and prevents surface degradation.

The surface chemical states of the synthesized cathodes were analyzed using X-ray photoelectron spectroscopy (XPS). After etching, the peak positions of Ni and Mn in NFMMT/NaCaPO₄ do not shift significantly, indicating that the TM ions are coordinated to O²⁻ rather than PO₄³⁻ (Fig. 2a and Supplementary Fig. 11a). Additionally, as the etching depth increases, the Ni and Mn peak intensities gradually increase and then stabilize, whereas the Ca peak intensity decreases significantly, confirming the presence of a NaCaPO₄ surface protective layer (Fig. 2b)³⁷. Furthermore, the high-resolution C 1s XPS spectrum was deconvoluted into two peaks at 284.4 and 288.3 eV, corresponding to CO₃²⁻ and C–C bonds, respectively (Fig. 2c). Notably, NFMMT/NaCaPO₄ exhibited a lower CO₃²⁻ intensity, indicating that the coating effectively consumes surface residual Na species, consistent with the low surface oxygen content observed in the high-resolution O 1s XPS spectrum (Supplementary Fig. 11b). The decrease in alkaline surface residual Na species (e.g., NaOH and Na₂CO₃) significantly enhances the air stability of the layered oxide cathodes¹⁸. Based on these results, thermodynamically driven Na/Ca ion exchange leads to the formation of a small amount of the P2 phase and gradient Ca²⁺ doped interphase. The elemental distribution within the particles was further visualized using time-of-flight secondary ion mass spectrometry (TOF-SIMS)²⁶. As shown in Fig. 1d–f, P is concentrated in the outer layer, while trace amounts of Ca²⁺ are present in both the outer and inner regions of the particles. These findings confirm the successful formation of a reconstructed layer, featuring a 10 nm NaCaPO₄ coating accompanied by gradient Ca²⁺ doping at the interface.

2.2 Na storage performance of surface-modified cathode

The electrochemical behavior of the prepared cathodes was first evaluated using a standard coin-type half cell within the voltage range of 2.0–4.2 V (vs. Na⁺/Na). As revealed by the voltage curves for the initial cycle at 0.1 C (1 C = 150 mA g^− 1), all the samples undergo similar electrochemical processes (Fig. 3a). The charge/discharge plateaus at approximately 2.7 and 4.1 V correspond to phase transitions from O3 to P3 and P3 to OP2, respectively, whereas the sloping region between 3.0 V and 4.0 V corresponds to the solid-solution reaction of the P3 phase.³³ Compared with NFM, which has a high discharge capacity of 177.1 mAh g^− 1, the incorporation of inactive Mg/Ti ions reduces the Ni content of NFMMT, resulting in a lower reversible capacity of 152.7 mAh g^− 1. The introduction of the NaCaPO₄ coating slightly decreased the reversible capacity of NFMMT/NaCaPO₄ to 148.2 mAh g^− 1, which remains within the acceptable range. However, NFMMT/NaCaPO₄ achieved the highest initial Coulombic efficiency (ICE) of 99% with a capacity loss of only 3.2 mAh g^− 1, thereby significantly outperforming the original sample (84.6% ICE and 32.4 mAh g^− 1 capacity loss). This high ICE is attributed to the in situ consumption of surface residual alkali species (NaOH and Na₂CO₃) during the coating formation process, which agrees with the XPS results³⁸. During cyclic voltammetry (CV) measurements at a scanning rate of 0.1 mV s^− 1, the redox peak position of NFMMT/NaCaPO₄ remains stable over the first 5 cycles, indicating that the reconstructed interface is beneficial for improving structural reversibility and inhibiting anionic redox reactions (Fig. 3b)¹⁶. In contrast, NFMMT exhibits a significantly reduced peak current intensity and pronounced separation of the redox peak potentials (0.223 V), suggesting that irreversible structural damage occurs during the electrochemical process. The rate capabilities of the synthesized cathodes were evaluated at different C rates (0.1–10 C and then returning to 0.2 C) (Fig. 3c). The capacity of NFMMT/NaCaPO₄ decays gradually under high current densities, but the initial discharge capacity is almost fully recovered after rate testing, with reversible capacities of 148.3, 142.8, 136.2, 130.5, 124.0, and 119.2 mAh g^− 1 at 0.1, 0.2, 0.5, 1, 2, and 5 C, respectively. Even at a high current rate of 10 C, NFMMT/NaCaPO₄ maintains a capacity of 105.3 mAh g^− 1, which is approximately 71.0% of the capacity at 0.1 C. In sharp contrast, the discharge capacities of the pristine and doped samples decrease dramatically with increasing current rate. The introduction of a protective layer with fast ion conductor characteristics enhances the Na-ion diffusion kinetics of the modified cathode, thereby improving the fast charging/discharging performance and reducing electrochemical polarization at high current rates (Supplementary Fig. 12).

Subsequently, the impact of the interface reconstruction strategy on long-term cycling stability was assessed using galvanostatic charge/discharge tests. As shown in Fig. 3d, NFMMT/NaCaPO₄ has the highest structural stability, with a high capacity retention of 81.0% after 300 cycles at 0.5 C, significantly outperforming NFM (58.6% capacity retention after 100 cycles) and NFMMT (61.5% capacity retention after 200 cycles). This remarkable improvement in cycling stability is attributed to the enhanced surface chemistry and bulk mechanical stability, as discussed in the following sections. Although the capacity retention of NFMMT-Ca doped (63.6% after 200 cycles) is slightly higher than that of NFMMT, it remains inferior to that of NFMMT/NaCaPO₄, suggesting that further doping in multicomponent cathodes hinders efficient Na storage²⁴. The prepared cathodes were further tested at high current densities of 1–5 C (Supplementary Figs. 13 and 14). NFMMT/NaCaPO₄ delivers terminal capacities of 122.8 and 108.1 mAh g^− 1 after 100 and 300 cycles at 1 C, corresponding to capacity retention rates of 94.4% and 83.1%, respectively (Fig. 3e). The long-term cycling stability of NFMMT/NaCaPO₄ at different current rates is consistent with its excellent rate performance, which is attributed to the high ionic conductivity and robust interfacial stability of the introduced coating. This outstanding Na storage performance surpasses most previously reported results, highlighting the progressive nature of the interface reconstruction strategy (Fig. 3f and Supplementary Table 3)^38–49.

The high-voltage performance (4.5 V), all-climate performance (− 10°C to 50°C), and air stability of the prepared cathode were evaluated to assess its operability in harsh environments. Even at a high cutoff voltage of 4.5 V (Supplementary Fig. 15), the optimized cathode delivers a reversible capacity of 109.9 mAh g^− 1 with a capacity retention of 71.2% after 150 cycles at 0.5 C, thereby significantly outperforming NFMMT (53.8% capacity retention). Additionally, because of their high surface reactivity and strong adsorption capacity, layered cathodes typically exhibit poorer air stability than their Li counterparts, which significantly limits their commercial potential^{8, 50}. However, after exposure to humid air for 7 days, the O3 phase structure of NFMMT/NaCaPO₄ is largely retained, with minimal byproduct formation and a small peak shift (0.133°), demonstrating that the uniform reconstruction layer effectively protected the cathode from water insertion (Supplementary Figs. 16 and 17). Consequently, the aged NFMMT/NaCaPO₄ maintains a reversible capacity of 130.5 mAh g^− 1 at 0.5 C, with 81.4% capacity retention after 150 cycles at 0.5 C (Fig. 3g). In contrast, exposure to moisture causes NFMMT to aggregate and form by-products, which increases interfacial resistance and hinders Na-ion diffusion kinetics, leading to poor Na storage performance, with a capacity retention of 68.0% after 150 cycles.

The cycling stabilities of the prepared cathodes were evaluated at an elevated temperature of 50°C to assess structural integrity²⁹. As shown in Fig. 3h, NFMMT/NaCaPO₄ exhibits significantly improved cycling stability in the voltage range of 2–4.2 V, maintaining a reversible capacity of 112.2 mAh g^− 1 (80.4% capacity retention) after 200 cycles at 0.5 C. The enhanced high-temperature stability is attributed to improved thermal properties, leading to higher exothermic peaks and reduced heat generation in the fully desodiated state (Supplementary Fig. 18), ultimately contributing to increased safety. However, NFMMT retains only 51.1% of its initial capacity under the same conditions owing to dissolution of the active materials and adverse TM-ion crosstalk effects²⁹.

In addition, the feasibility of low-temperature (− 10°C) operation was evaluated to expand the application range of SIBs (Fig. 3i). Low temperatures limit ion mobility, leading to a relatively low discharge capacity and significantly increased polarization in the synthesized cathode (Supplementary Fig. 19)¹⁴. NFMMT delivers reversible capacities of 123.7, 111.4, and 90.3 mAh g^− 1 at 0.1, 0.2, and 1 C, respectively, indicating inferior rate performance at low temperatures. Encouragingly, NFMMT/NaCaPO₄ not only exhibits better rate performance at low temperatures (discharge capacities of 129.6, 116.9, and 108.6 mAh g^− 1 at 0.1, 0.2, and 1 C, respectively) but also demonstrates excellent cycling stability, retaining 90.1% of its initial capacity after 200 cycles at 0.5 C. However, the low-temperature performance of the bulk Ca-doped sample is worse than that of the NFMMT cathode, with a capacity retention of only 62.1% after 200 cycles. This behavior is attributed to the poor reaction kinetics caused by homogeneous Ca²⁺ doping in the Na layer, which hinders Na-ion diffusion³².

To obtain further insights into the improvement in low-temperature performance provided by the reconstructed coating, a cathode with a Na₃PO₄ coating (NFMMT/Na₃PO₄) was synthesized using a similar method. The introduced phosphate coating enhanced Na-ion diffusion kinetics, resulting in a cathode with a rate capability (110.0 mAh g^− 1 at 0.5 C) comparable to that of NFMMT/NaCaPO₄ but slightly inferior cycling stability. These findings indicate that surface-gradient Ca²⁺ doping significantly enhances interfacial structural stability and extends cycle life, as discussed in subsequent sections. Therefore, the optimized cathode demonstrates excellent cyclability under harsh conditions, including high cutoff voltages, humid air, and a wide temperature range.

Owing to the exceptional Na storage performance of NFMMT/NaCaPO₄ in Na half cells, this cathode was integrated into Na-ion full cells (with commercial hard carbon (HC) anodes) and anode-free cells (with carbon-coated Al (Al-C) anode current collectors) to assess its practical applicability⁵¹. To compensate for the initial capacity loss (Supplementary Figs. 20 and 21), electrochemical presodiation and sacrificial cathode additives were employed to preactivate HC and Al-C (see the methods section for details). As shown in Supplementary Fig. 22, the constructed full cell delivers a reversible capacity of 147.0 mAh g^− 1 (based on the cathode mass) at 0.1 C, with an average operating voltage of 3.16 V. The NFMMT/NaCaPO₄//HC full cell exhibits enhanced rate performance, achieving a high reversible capacity of 92.8 mAh g^− 1 at 10 C, whereas the NFMMT//HC full cell only reaches 66.1 mAh g^− 1 at the same rate (Fig. 4a). Additionally, the cycling stability of the full-cell system is promising. Specifically, the NFMMT/NaCaPO₄//HC full cell delivers an acceptable specific capacity of 138.3 mAh g^− 1 at 0.5 C, with a capacity loss of only 15% after 200 cycles (Fig. 4b). Even after 500 cycles at 1 and 2 C, 76.5% and 75.3% of the reversible capacity are retained, respectively (Fig. 4c). In contrast, the NFMMT//HC full cell retains only 59.6% of its initial capacity after 200 cycles at 0.5 C.

Owing to the absence of active materials on the anode side, anode-free Na batteries, which have ultrahigh energy densities, have recently garnered significant research attention⁴³. After activation^{52, 53}, the anode-free Na battery exhibits stable cycling with a reversible capacity of approximately 145 mAh g^− 1 (Supplementary Fig. 23). Owing to the detrimental crosstalk effect of TM ions derived from dissolution of the active materials⁵⁴, NFM//Al-C exhibits significant capacity degradation and inferior rate properties, delivering specific capacities of 166.2 and 65.4 mAh g^− 1 at 0.1 and 5 C, respectively (Fig. 4d). In contrast, NFMMT/NaCaPO₄//Al-C maintains a high reversible capacity of 96.9 mAh g^− 1 at 5 C, demonstrating effective suppression of TM dissolution. Additionally, long-term cycling durability tests showed that NFMMT/NaCaPO₄//Al-C retains 80.8% of its initial capacity after 300 cycles at 0.5 C, whereas NFM//Al-C lost 83.8% of its reversible capacity after 200 cycles (Fig. 4e). The enhanced cycling stability of NFMMT/NaCaPO₄//Al-C is particularly evident at high current rates, with 74.5% capacity retention after 500 cycles at 1 C (Fig. 4f). In contrast, NFM//Al-C loses nearly all of its capacity within the first 100 cycles.

As a demonstration of the practical feasibility of the proposed cathodes, single-layer pouch cells were assembled under realistic conditions using a high cathode loading (12 mg cm^− 2) and an HC anode without presodiation treatment^{30, 55}. Because of the initial irreversible capacity loss of the HC anode, the reversible capacity of the pouch cell (approximately 120 mAh g^− 1) is slightly lower than that of the half cell (Fig. 4g). However, the NFMMT/NaCaPO₄//HC pouch-type full cell retains 82.9% of its initial specific capacity after 300 cycles at a current density of 1.8 mA cm^− 2 (1 C), whereas the capacity retention of the NFM//HC pouch-type full cell is only 53.9% (Fig. 4h). Thus, the proposed NFMMT/NaCaPO₄ cathode exhibits excellent Na storage performance and has considerable potential for practical applications.

2.3 Structural evolution and reaction mechanism

The improved cycling stability of layered oxides is typically associated with structural evolution during electrochemical processes^{11, 30}. Consequently, in situ XRD analysis was used to evaluate the phase transitions of the NFMMT and NFMMT/NaCaPO₄ cathodes. Supplementary Fig. 24 illustrates that the prepared cathodes undergo a phase transition from hexagonal O3 to hexagonal P3, subsequently transitioning to OP2 phase.¹⁸ As shown in Fig. 5a, for both cathodes, the (003) diffraction peak shifts toward lower diffraction angles during initial charging and then abruptly to higher angles upon charging to approximately 4.0 V. Initially, Na extraction increases the electrostatic repulsion between adjacent oxygen slabs, resulting in an expansion of the c-lattice parameters²⁹. However, at high voltages and low Na contents, peroxo-like (O–O)ⁿ⁻ dimers reduce interlayer repulsion, leading to lattice contraction, which is characteristic of the phase transition from P3 to the OP2 phase with TMO₂ stacking faults³⁴. Notably, the shift of the (003) peak becomes asymmetric at the end of the charging stage (4.0–4.2 V) and during initial discharging (4.2–3.9 V). This behavior is attributed to ion transport being more rapid in the prismatic (P) layer than in the octahedral (O) layer, which results in the partial loss of O structures⁵. Obviously, NFMMT/NaCaPO₄ displays a more symmetrical shift during sodiation/desodiation (0.067° deviation), indicating enhanced structural reversibility. Although the structural evolution of both cathodes is similar, the specific changes in the lattice parameters during charging and discharging differ. As shown in Fig. 5b and Supplementary Fig. 25, smooth variations along the a-axis are accompanied by zigzag changes in the c and V parameters¹⁴. The change in the c-axis parameter is significantly smaller for NFMMT/NaCaPO₄ (7.2%) than for NFMMT (9.6%). Repeated fluctuations in the lattice parameters and sliding of the TMO₂ layer during electrochemical processes lead to the accumulation of internal stress and weakening of the repulsive force between the Na and TM layers, resulting in structural degradation and irreversible capacity loss^{29, 56}. Therefore, the reduced lattice parameter changes observed for NFMMT/NaCaPO₄ indicate enhanced structural stability and integrity.

To clarify the underlying mechanism, the evolution of the (003) peak during the O3–P3 phase transition was examined in detail. As shown in Fig. 5c, NFMMT displays distinct and well-defined O3 and P3 regions, which are attributed to the uneven extraction of Na from the particles. An uneven Na-ion distribution can lead to the coexistence of two phase regions with significantly different lattice parameters, resulting in lattice mismatch, the accumulation of internal stress, and structural degradation²². In contrast, for NFMMT/NaCaPO₄, the (003) peak has a coexisting intermediate phase at 2.8 V, indicating a more uniform phase transition and reduced Na-ion concentration gradient (Fig. 5d). This uniform phase transition, combined with a low Na-ion concentration gradient, effectively prevented Na-ion blockage within the particles and promoted orderly structural evolution.

Electrochemical impedance spectroscopy (EIS) and the galvanostatic intermittent titration technique (GITT) were used to evaluate the effect of the reconstruction layer on the reaction kinetics⁵⁷. In the GITT measurements, current pulses of 0.05 C were applied for 1200 s, followed by a 2 h relaxation period³³. All the cathodes exhibit lower Na⁺ diffusion coefficients (D_Na) at approximately 2.8 and 4.1 V, which is attributed to phase transitions caused by interlayer slipping (Fig. 5e). NFMMT/NaCaPO₄ has significantly higher D_Na values (3.72 × 10^− 11–4.64 × 10^− 10 cm² s^− 1) and a lower overpotential (≈ 15 mV) (Supplementary Fig. 26), indicating that the interface coating effectively enhanced the ion diffusion kinetics. This result is consistent with the D_Na value calculated from the CV results using the linear relationship between the peak current and square root of the scan rate (Supplementary Fig. 27). Specifically, owing to the fast ion conductor coating, the D_Na value of NFMMT/NaCaPO₄ (4.20 × 10^− 10 cm² s^− 1) is nearly twice that of NFMMT (2.21 × 10^− 10 cm² s^− 1). Notably, the Ca-doped sample exhibits lower Na⁺ diffusivity because the Ca²⁺ ions incorporated into the interlayer partially hinder Na-ion diffusion, consistent with its relatively poor rate performance and low-temperature behavior. However, as the amount of Ca²⁺ introduced into the Na layer is small, the gradient doping strategy has a minimal negative impact on the reaction kinetics. Consequently, the customized interface reconstruction layer effectively enhances the long-term cycling stability of layered oxides without compromising rate performance, which is essential for developing commercial cathodes.

Electrode degradation after long-term cycling was investigated by analyzing the EIS spectra of the cathode at different states of charging (SOC). As shown in Supplementary Fig. 28–30, the Nyquist plots consist of semicircles in the high- and mid-frequency regions and a sloped line in the low-frequency region, corresponding to the surface diffusion resistance (R_sf), charge-transfer resistance (R_ct), and Warburg diffusion impedance, respectively²². The R_ct value is higher than the R_sf value, indicating that charge-transfer resistance plays a greater role in the electrochemical behavior of layered oxides³³. Compared with NFMMT and NFMMT-Ca doped, NFMMT/NaCaPO₄ has lower R_ct values throughout the electrochemical process owing to the introduction of a surface protective layer (Supplementary Fig. 31)¹⁵. However, parasitic side reactions and structural degradation cause the R_ct value to increase with cycling (Fig. 5f). Nevertheless, the R_ct value of NFMMT/NaCaPO₄ increases by only 80.7 Ω after 200 cycles, which is significantly lower than the increases observed for NFMMT (241.9 Ω) and NFMMT-Ca doped (344.5 Ω). These results confirm that the introduced interface reconstruction layer enhances ionic transport and mitigates the intergranular cracking and structural degradation caused by phase transitions, leading to improved cathode durability.

The impact of the interface reconstruction strategy on the structural integrity of layered oxide cathodes was explored using cross-sectional SEM analysis. As shown in Fig. 5g, after 200 cycles, prominent cracks penetrate the NFMMT particles, which are attributed to stress accumulation at the grain boundaries and intergranular crack formation along the c-axis owing to lattice parameter variations and dislocations during the electrochemical process^{6, 58}. These microcracks expose fresh surfaces, thereby accelerating electrolyte penetration and leading to the formation of unstable cathode electrolyte interphase (CEI) layers, consistent with the obvious increase in electrochemical impedance²⁹. In contrast, NFMMT/NaCaPO₄ exhibits negligible structural damage, even after 200 cycles, demonstrating a strengthened crystal structure and improved mechanical integrity (Fig. 5h). Similarly, XRD analysis (Supplementary Fig. 32) reveals that cycled NFMMT/NaCaPO₄ largely retains its initial crystal structure, with minimal changes in the lattice parameters (0.048° shift of the (003) peak). In contrast, NFMMT exhibits a notable shift in the (003) peak toward lower diffraction angles (0.113°) and the formation of a trace amount of a Na-deficient phase, indicating lattice expansion and irreversible loss of active Na after prolonged cycling. This behavior is a key indicator of structural degradation and capacity decay⁵⁹.

Given the critical role of the interface structure in the cycling stability of layered cathode materials, the surface chemical properties of the electrodes after 200 cycles at a fully charged state (4.2 V) were investigated in detail to highlight the effectiveness of surface engineering (Fig. 6). The SAED pattern of the cycled NFMMT/NaCaPO₄ exhibits typical O3 phase characteristics along the [100] zone axis, indicating the preservation of high crystallinity (Fig. 6f). In contrast, the blurred diffraction spots in the cycled NFMMT suggest unfavorable phase transitions from the layered to the rock-salt phase (Fig. 6b). Cross-sectional TEM imaging reveals significant damage on the surface of the fully charged NFMMT cathode after extended cycling, with cracks that are approximately 50 nm deep and 5 nm wide (Fig. 6d). In addition, parasitic reactions and electrolyte corrosion led to the formation of an insulating rock salt layer with a thickness of approximately 16 nm on the particle surfaces, as confirmed by the corresponding fast Fourier transform (FFT) pattern¹¹. Even within the particles, the accumulation of internal stress induced by non-uniform phase transitions and interlayer slip can result in the formation of intragranular cracks and kinking of delaminated layers (Fig. 6c)^{30, 60}. This surface degradation and mechanical damage hinder Na-ion transport, limits the utilization of active materials, and contributes to irreversible capacity loss in NFMMT. Notably, the interface and bulk structures of NFMMT/NaCaPO₄ are nearly intact after cycling, indicating enhanced mechanical integrity (Fig. 6e). Additionally, the reconstructed layer that integrates the coating and gradient Ca²⁺ doped interphase remains apparent after extended cycling, effectively preserving the integrity and order of the original O3-type structure and thus enhancing the long-term Na storage performance (Fig. 6g,h and Supplementary Fig. 33)¹⁴. Additionally, the EDS line scan results indicate a gradual increase in the Na-ion concentration from the surface to the core, stabilizing at approximately 90 nm (Fig. 6i), which directly demonstrates the presence of an ion concentration gradient within the NFMMT particles at the fully charged state. In contrast, the Na-ion concentration in NFMMT/NaCaPO₄ is relatively uniform, indicating that the introduced interface reconstruction layer effectively reduces the Na-ion concentration gradient (Fig. 6j)²⁵. To further investigate the structural inhomogeneity within the particles, the average interlayer spacing from the edge to the core was quantitatively assessed using HRTEM and SAED patterns (Supplementary Fig. 34). As shown in Fig. 6k, the interlayer spacing near the edge of NFMMT is relatively small (15.77 Å), corresponding to the OP2 phase in the deep sodiation state, whereas the maximum value (16.28 Å) appears at the center, indicating the presence of two distinct structures with different lattice parameters within the particles⁶¹. This structural inhomogeneity generates uneven stress, which is released through dislocations and slips during electrochemical cycling, resulting in microcrack formation¹⁹. Interestingly, the interlayer spacing difference within the NFMMT/NaCaPO₄ particles is significantly smaller (0.209 Å) than that within the NFMMT particles (0.507 Å), indicating a reduction in structural mismatch. Therefore, the interface reconstruction layer effectively enhances the mechanical stability of layered oxides by reducing the Na-ion concentration gradient and promoting uniform phase transitions.

The surface chemical states of the cycled electrodes were characterized using XPS. As shown in Supplementary Fig. 35a, CF_x bonds related to polyvinylidene fluoride (PVDF) and NaF species formed by electrolyte decomposition were detected on the surface of the cycled electrodes²⁹. Notably, NFMMT exhibits a higher content of NaF and (CF_x) byproducts, suggesting that electrolyte decomposition on this cathode results in the formation of a thicker CEI layer (Supplementary Fig. 35b). Even after 200 cycles, strong phosphate signals were detected on the surface of NFMMT/NaCaPO₄, demonstrating the electrochemical stability of the reconstructed layer (Supplementary Fig. 35c). TOF-SIMS measurements provided 3D distribution and depth profile data, revealing an enriched phosphate (PO²⁻) coating on NFMMT/NaCaPO₄ (Fig. 6l). Additionally, NFMMT/NaCaPO₄ contained a lower content of organic components (C₂HO⁻) and metal fluorides (NaF₂⁻ and MnF₃⁻) resulting from interface degradation and surface side reactions in NFMMT (Fig. 6m,n and Supplementary Fig. 34d,e), demonstrating that the protective layer effectively suppresses adverse parasitic reactions between the cathode and electrolyte²².

To further elucidate the role of the interface reconstruction layer, core–shell-structured cathodes with various coating layers (Na₃PO₄ and NaXPO₄, where X = Ba, Sr, Cu, Mg, Sb, or Al) were synthesized (Supplementary Fig. 36). As shown in Supplementary Fig. 37, the introduced polyanionic coatings effectively enhance the ion diffusion kinetics. Consequently, all the coated samples exhibit better Na storage performance than NFMMT^{18, 38}. Notably, the Na₃PO₄ coating significantly enhances the reaction kinetics of the layered cathode, yielding better rate performance than NFMMT/NaCaPO₄ (Supplementary Fig. 38). The straightforward surface coating strategy using Na₃PO₄ enhance the electrochemical performance by facilitating Na-ion diffusion and improving the interfacial stability³⁸. However, the introduction of incompatible cations with relatively large ionic radii or high valence states into the Na layer negatively affects cycling performance (Fig. 7a and Supplementary Fig. 39)³⁰. Therefore, these surface-modified cathodes exhibit similar suboptimal cycling stabilities. Interestingly, the introduction of Ca²⁺, Cu²⁺, and Mg²⁺, which have greater compatibility with Na⁺, markedly improves the cycling stability of NFMMT, with the NaCaPO₄-coated cathode demonstrating the best cycling performance. Notably, the cycling stabilities of the samples with bulk Ca²⁺ doping and/or a surface Na₃PO₄ coating remain inferior to that of NFMMT/NaCaPO₄ (Supplementary Fig. 40), suggesting that gradient Ca²⁺ doping plays a critical role in enhancing structural stability.

Further insights into the role of the Ca dopant were obtained using density functional theory (DFT) calculations, which disregarded the influence of the coating layer. Figure 7b illustrates the lattice-matching relationship between fresh NFMMT (F-NFMMT) and partially desodiated NFMMT (P-NFMMT) at 20% SOC, highlighting the lattice mismatch caused by uneven Na extraction. After the introduction of Ca²⁺ into partially desodiated NFMMT (P-NFMMT-Ca), the binding energy between the partially charged and pristine structures decreases from − 0.53 eV to − 3.87 eV. This reduction indicates that Ca²⁺ incorporation significantly alleviates the internal stress caused by lattice mismatch, thereby enhancing the structural stability of the layered framework during desodiation. Differential charge density analysis revealed the localized effects of the Ca²⁺ dopant in P-NFMMT (Fig. 7c). In the charge density map, cyan and yellow represent areas of decreased and increased electron density, respectively. The electron density around the Ca²⁺ ions is significantly reduced, whereas the adjacent oxygen atoms exhibit increased electron density. Furthermore, density of state (DOS) calculations (Supplementary Fig. 41) were performed to elucidate this energy difference. Compared with F-NFMMT, P-NFMMT exhibits a shift in electron density from the valence band to the conduction band owing to the removal of Na ions. However, the introduction of Ca²⁺ mitigates this shift to some extent, resulting in a smaller difference in the electron distribution before and after desodiation. This optimization of the electron distribution is beneficial for reducing the local energy differences caused by uneven Na extraction. These results indicate a strong interaction between Ca and O, which stabilizes the interlayer structure of the TMO₂ framework, mitigating structural changes during desodiation process. Additionally, the Ca–O interaction effectively suppresses oxygen release, thereby enhancing the structural stability under high-voltage conditions.

Simulations of the Na⁺ distribution and stress evolution in NFMMT and NFMMT/NaCaPO₄ were conducted using COMSOL. As illustrated in Supplementary Fig. 42, surface Na ions are preferentially released over internal Na ions. Nonetheless, NFMMT/NaCaPO₄, with its uniform phase transition, contains a relatively uniform distribution of Na ions throughout the electrochemical process. In contrast, the uneven phase transition and kinetic differences in NFMMT lead to significant Na-ion concentration gradients, particularly pronounced in the phase transition region (charged to approximately 3.0 and 4.2 V). This concentration gradient results in the accumulation of internal stress and microcrack formation. Notably, NFMMT, characterized by a pronounced Na-ion concentration gradient, displays a marked stress distribution (especially in the fully charged state), which is a key contributor to rapid capacity decay (Fig. 7d). Conversely, minimal internal stress is generated in NFMMT/NaCaPO₄ during the electrochemical process, resulting in enhanced structural integrity and an extended cycle life (Fig. 7e). Therefore, the proposed interface reconstruction layer facilitates the construction of stable layered oxide cathodes by reducing the Na-ion concentration gradient, ensuring uniform phase transitions, and minimizing internal stress.

The precisely designed interface reconstruction layer has multiple functions: 1) in situ consumption of surface residual Na species to enhance resistance to humid air; 2) creation of fast ion diffusion channels to improve rate performance; 3) formation of a protective coating to mitigate parasitic reactions with the electrolyte, thereby enhancing the chemical and thermal stabilities; and 4) gradient Ca²⁺ doped interphase to promote a uniform phase structure and Na-ion concentration within the particles, alleviate internal stress, and minimize microcrack formation, thereby enhancing the mechanical stability (Fig. 8a). As a result, the modified cathode with enhanced chemical/mechanical stability demonstrates excellent Na storage performance and practical feasibility for both Na-ion full cells and anode-free cells.

Furthermore, to validate its versatility, the interface reconstruction strategy was applied to other layered oxides with different Ni contents. As shown in Supplementary Fig. 43, the specific capacity of the layered cathode is closely related to the active Ni content. However, high discharge capacities often lead to large lattice parameter changes and structural degradation, resulting in reduced cycling stability. Fortunately, the introduction of an interface reconstruction layer enhanced the chemical and mechanical stabilities of the layered cathodes, leading to a significantly extended cycle life for each coated cathode (Fig. 8b). Therefore, the proposed interface reconstruction strategy can effectively improve the Na storage performance of various layered oxide cathodes, providing a valuable approach for the development of high-performance cathode materials for SIBs (Fig. 8c).

In summary, this study successfully integrated a customized reconstruction layer onto the surface of O3-type cathodes using a wet chemistry method to address the challenges of interface instability and mechanical degradation. The protective coating enhanced the rate performance and air/thermal stability of the layered cathode by providing fast ion diffusion channels, consuming surface residual Na species, and suppressing parasitic side reactions. Furthermore, gradient Ca²⁺ doping reduced internal stress accumulation and enhanced structural integrity by promoting uniform phase transitions and minimizing Na-ion concentration gradients. Consequently, the optimized cathode achieved excellent rate performance (105.3 mAh g^− 1 at 10 C) and long-term cycling stability (81.0% capacity retention after 300 cycles at 0.5 C), as well as robust cyclability under extreme conditions, including high voltage (4.5 V), high temperature (50°C), and low temperature (− 10°C). This interface reconstruction strategy, which was also successfully applied to other layered oxide cathode materials, broadens the scope of interface optimization and provides valuable insights into the development of next-generation advanced cathodes for SIBs.

Synthesis of Na layered cathode materials

NFM, NFMMT, and NFMMT-Ca doped were synthesized by a simple solid-state method. Stoichiometric amounts of CH₃COONa (3 mol.% excess, 99%), Ni(CH₃COO)₂ (99%), Fe(NO₃)₃·9H₂O (98%), Mn(CH₃COO)₂ (98%), Mg(NO₃)₃ (99%), TiO₂ (99%), Ca(NO₃)₂ (99%), and C₆H₈O₇ (chelating agent, 3 g) were dispersed in ethanol and mixed thoroughly in a ball mill for 24 h. The mixture was dried at 80°C, ground, and then calcined under an oxygen atmosphere (450°C for 5 h and 900°C for 12 h) to obtain the final product. For comparison, a series of cathode materials with varying compositions and contents was synthesized using a similar method.

Synthesis of coated samples

As-prepared NFMMT cathodes were mixed with the desired amount (1, 3, or 5 mol% relative to the total mass of the cathode material) of Ca(NO₃)₂ (Aladdin) in ethanol (99.8%). The resulting solution was magnetically stirred for 20 min. After dropwise addition of a phosphoric acid solution (0.05 M H₃PO₄ (Aladdin) in ethanol), the mixture was stirred for 1 h, followed by evaporation at 120°C for 10 h. The obtained powder was ground and calcined under an oxygen atmosphere at 650°C for 5 h to produce the coated sample. For comparison, the composition of the coating layer was adjusted by varying the type of cation used in the above procedure. All synthesized cathodes were stored in an Ar-filled glove box with H₂O and O₂ levels below 0.1 ppm.

Structural characterization

The compositions of the prepared cathode materials were determined using ICP-OES (Optima 8300, PerkinElmer). The crystallographic structure was examined using XRD (Empyrean, Panalytical) with a Cu Kα radiation source. In situ XRD experiments were performed in transmission mode on pouch-type half cells cycled between 2.0 and 4.2 V at 0.05 C (7.5 mA g^− 1). The XRD data were processed using Rietveld refinement software (FullProf). XPS (PHI5600, Physical Electronics) was used to analyze the oxidation states of the components. The cycled cathodes were retrieved, cleaned with dimethyl carbonate, and vacuum dried prior to analysis. To prevent exposure to moisture, the cathodes were protected with ketone films. Microscopic analysis of the cathode materials was performed using SEM (Nova Nano SEM 450, FEI) and Cs-corrected TEM (JEM-ARM200F, JEOL). The SEM and TEM samples were prepared by electrode polishing with a cross-sectional polisher (SM-09010, JEOL) and milling with an FIB (FIB, JEM-2100F, JEOL), respectively. The thermal stabilities of the desodiated cathodes in the electrolyte were evaluated using DSC (Thermo Plus, Rigaku). The spatial distribution of constituent elements (Ni, Fe, Mn, Ca, P, and F) across the cathode cross sections was examined using TOF-SIMS (TofWerk). A TOF.SIMS5 mass spectrometer (IONTOF) equipped with a 30 keV Bi⁺ primary ion beam and a 500 eV Cs⁺ sputter source was used to analyze the depth profiles of the cycled cathodes, with a sputtering area of 400 × 400 µm².

Electrochemical tests: Slurries containing 85 wt.% active material, 10 wt.% conducting agent (carbon black, Alfa Aesar), and 5 wt.% PVDF (Solef 5130, Solvay) dispersed in N-methyl-2-pyrrolidone were cast on Al foils and dried at 110°C for 10 h to produce cathodes (working electrodes). Electrode preparation was conducted in a controlled environment (25°C, dew point lower than − 60°C) to prevent exposure to moisture. The average active material loading on the cathode was 3.6 mg cm^− 2. Coin-type half cells were assembled in a glove box using a high-purity Na sheet as the counter electrode with an electrolyte, separator (glass fiber), and working electrode. The electrolyte consisted of 1 M NaPF₆ in propylene carbonate with 2 vol.% fluoroethylene carbonate as an additive. To assess the electrochemical performance of the cathodes, galvanostatic charge–discharge tests (TOSCAT-3100U, Toyo System) and CV (VMP3, Bio-Logic) were conducted within a voltage range of 2.0–4.2 V (vs. Na⁺/Na; 1 C = 150 mA g^− 1). Similar assemblies with commercial HC anodes and commercially available Al-C anode collectors were used for Na-ion full cells and anode-free cells, respectively. In these cells, the initial irreversible capacity loss was mitigated by presodiation of the HC anode or addition of a sacrificial agent (Na₂C₂O₄) to the cathode. Specifically, the HC anode for the coin-type full cell was pretreated to a fully sodiated state. For the cathode in the anode-free cell, 17 wt.% Na₂C₂O₄ was added to the slurry before casting. The anode-free cells were assembled with the Na₂C₂O₄-containing cathode, an Al-C anode collector, and glass fiber and activated between 2.0 and 4.7 V for one cycle before regular cycling. For the pouch-type Na-ion full cells, a prepared cathode (3 × 5 cm², mass loading: 12 mg cm^− 2) was paired with an HC anode, with the negative electrode capacity set to approximately 1.1 times that of the positive electrode (N/P = 1.1). The operating voltage ranges were 1.9–4.19 V for the Na-ion full cells and 2.0–4.2 V for the anode-free cells. GITT and EIS (IM6, Zahner Elektrik) were performed to determine the Na-ion diffusion coefficients and evaluate the electrochemical kinetics of the prepared cathodes.

Modeling

DFT implemented in CP2K/Quickstep1 was used to study the impact of Ca on the system. The Perdew–Burke–Ernzerhof (PBE) functional was used to describe the exchange–correlation effects, and dispersion correction was applied in all calculations using the Grimme D3 method. The ΔE values were calculated using the following equation

ΔE = E_total − E₁ − E₂

where E_total is the energy of the interfacial model, E₁ is the energy of F-NFMMT, and E₂ is the energy of P-NFMMT or P-NFMMT-Ca. The Hubbard parameter (U_eff =3.90 eV) was added to correct for the strong correlation of the TM. Brillouin zone integration was conducted by employing Γ 1 × 1 × 1 for geometric optimization. An auxiliary plane-wave basis set with a cutoff value of 400 Ry was used to compute the electrostatic terms. The structure of the P-NFMMT-Ca system was simulated by displacing some Na atoms (two Na atoms for each Ca atom) based on the normal P-NFMMT model. The interface was modeled based on the XRD results.

Finite element analysis was conducted using COMSOL Multiphysics to simulate the evolution of stress–strain and the Na-ion distribution during the cycling of NFMMT and NFMMT/NaCaPO₄. The Na⁺ concentration within the cathode particles was modeled using Fick's second law: (∂c_Na/∂_t = − D∇²c_Na), where D represents the Na⁺ diffusion coefficient, which was obtained from GITT measurements. Key parameters were set as follows: thermal conductivity at 1.58 W m^− 1 K^− 1, electrical conductivity at 0.17 S m^− 1, density at 1.5 g cm^− 3, and specific heat capacity at constant pressure at 840.1 J kg^− 1 K^− 1. The particle model size closely matched the actual crystal particles observed by SEM, with an approximate size of 2 µm.

Reporting summary

Further information on research design is available in the Nature Portfolio Reporting Summary linked to this article.

Reporting summary

Further information on research design is available in the Nature Portfolio Reporting Summary linked to this article.

Data availability

The authors declare that all relevant data supporting the findings of this work are included in the Article, with additional data provided in the Supplementary Information. The datasets generated during the current study are available from the corresponding author on reasonable request.

Acknowledgements

This work was supported by the Human Resources Development Program (No. 20214000000320) of the Korea Institute of Energy Technology Evaluation and Planning (KETEP), funded by the Ministry of Trade, Industry, and Energy of the Korean government. This work was also supported by Korea Institute of Energy Technology Evaluation and Planning (KETEP) grant funded by the Korea government (MOTIE) (RS-2024-00398346, ESS Big Data-Based O&M and Asset Management Technical Manpower Training).

Author information

Authors and Affiliations

Department of Energy Engineering, Hanyang University, Seoul, South Korea

Xinghui Liang, Xiaosheng Song, Hun Kim, Myoung-Chan Kim & Yang-Kook Sun

Department of Chemical and Biological Engineering, University of Alabama, Alabama, USA

H. Hohyun Sun

Department of Battery Engineering, Hanyang University, Seoul, South Korea

Yang-Kook Sun

Contributions

Xinghui Liang and Prof. Yang-Kook Sun conceived the idea. Xinghui Liang conducted the experiments and drafted the original manuscript. Xiaosheng Song conducted the theoretical calculations, assisted with in situ tests, and analyzed the corresponding data. H. Hohyun Sun, Hun Kim, and Myoung-Chan Kim contributed to the discussion of the results. Prof. Yang-Kook Sun supervised the project and provided financial support. All authors contributed to the discussion and revision of the manuscript.

Corresponding author

Correspondence to Yang-Kook Sun.

Competing interests

The authors declare no competing interests.

Liang X, Hwang J-Y, Sun Y-K (2023) Practical cathodes for sodium-ion batteries: Who will take the crown? Adv Energy Mater 13:2301975
Hwang J-Y, Myung S-T, Sun Y-K (2017) Sodium-ion batteries: present and future. Chem Soc Rev 46:3529–3614
Hwang J-Y et al (2015) Radially aligned hierarchical columnar structure as a cathode material for high energy density sodium-ion batteries. Nat Commun 6:6865
Sada K, Kmiec S, Manthiram A (2024) Mitigating sodium ordering for enhanced solid solution behavior in layered NaNiO₂ cathodes. Angew Chem Int Ed 136:e202403865
Yu T-Y et al (2023) High-voltage stability of O3-type sodium layered cathode enabled by preferred occupation of Na in the OP2 phase. Energy Storage Mater 61:102908
Yu T-Y, Ryu H-H, Han G, Sun Y-K (2020) Understanding the capacity fading nechanisms of O3-type Na[Ni_0.5Mn_0.5]O₂ cathode for sodium-ion batteries. Adv Energy Mater 10:2001609
Ryu H-H, Park K-J, Yoon CS, Sun Y-K (2018) Capacity fading of Ni-rich Li[Ni_xCo_yMn_1–x–y]O₂ (0.6 ≤ x ≤ 0.95) cathodes for high-energy-density lithium-ion batteries: Bulk or surface degradation? Chem Mater 30:1155–1163
Yang Y et al (2024) Decoupling the air sensitivity of Na-layered oxides. Science 385:744–752
Lee S et al (2021) Direct observation of the in-plane crack formation of O3-Na_0.8Mg_0.2Fe_0.4Mn_0.4O₂ due to oxygen gas evolution for Na-ion batteries. J Mater Chem A 9:14074–14084
Guo Y-J et al (2021) Boron-doped sodium layered oxide for reversible oxygen redox reaction in Na-ion battery cathodes. Nat Commun 12:5267
Feng S et al (2024) Surface engineering through in situ construction of Co_xB-spinel dual coating layers for high-voltage stable sodium-ion batteries. Adv Energy Mater 14:2303773
Wang H et al (2024) Manipulating local chemistry and coherent structures for high-rate and long-life sodium-ion battery cathodes. ACS Nano 18:13150–13163
Liu R et al (2024) Revealing the nature of binary-phase on structural stability of sodium layered oxide cathodes. Adv Mater 36:2401048
Li X et al (2023) Multi-level modifications enabling chemomechanically stable Ni-rich O3-layered cathode toward wide-temperature-tolerance quasi-solid-state Na-ion batteries. Adv Energy Mater 13:2203701
Hong N et al (2023) An in situ dual-modification strategy for O3-NaNi_1/3Fe_1/3Mn_1/3O₂ towards high-performance sodium-ion batteries. J Mater Chem A 11:18872–18880
Xia X et al (2022) Suppressing the dynamic oxygen evolution of sodium layered cathodes through synergistic surface dielectric polarization and bulk site-selective Co-doping. Adv Mater 35:2209556
Yu Y et al (2021) Revealing the anionic redox chemistry in O3-type layered oxide cathode for sodium-ion batteries. Energy Storage Mater 38:130–140
Xu W et al (2023) Conversion of surface residual alkali to solid electrolyte to enable Na-ion full cells with robust interfaces. Adv Mater 35:2301314
Chae B-G, Park SY, Song JH, Lee E, Jeon WS (2021) Evolution and expansion of Li concentration gradient during charge-discharge cycling. Nat Commun 12
Yang J, Liang X, Ryu H-H, Yoon CS, Sun Y-K (2023) Ni-rich layered cathodes for lithium-ion batteries: From challenges to the future. Energy Storage Mater 63:102969
Gao Z et al (2024) Kirkendall effect-induced uniform stress distribution stabilizes nickel-rich layered oxide cathodes. Nat Commun 15:1503
Wang W et al (2024) Surface atomic rearrangement with high cation ordering for ultra-stable single-crystal Ni-rich Co-less cathode materials. Adv Funct Mater, 2409956
Yin X et al (2024) Synergetic modulation of interlayer–intralayer spacings for P2-type layered oxide cathode with superior rate performance. ACS Energy Lett 9:3922–3930
Li R et al (2024) High-entropy and multiphase cathode materials for sodium-ion batteries. Adv Energy Mater 14:2400127
Jiang N et al (2024) Surface gradient desodiation chemistry in layered oxide cathode materials. Angew Chem Int Ed 63:e202410080
Jo CH et al (2018) Bioinspired surface layer for the cathode material of high-energy-density sodium-ion batteries. Adv Energy Mater 8:1702942
Ou X et al (2018) Mn doped NaV₃(PO₄)₃/C anode with high-rate and long cycle-life for sodium ion batteries. Energy Storage Mater 12:153–160
Gao X et al (2023) Post-substitution modulated robust sodium layered oxides. Small Methods 7:2300635
Liang X, Sun Y-K (2022) A novel pentanary metal oxide cathode with P2/O3 biphasic structure for high-performance sodium-ion batteries. Adv Funct Mater 32:2206154
Ding F et al (2024) Tailoring planar strain for robust structural stability in high-entropy layered sodium oxide cathode materials. Nat Energy
Yu T-Y, Sun Y-K (2022) A fluorinated O3-type layered cathode for long-life sodium-ion batteries. J Mater Chem A 10:23639–23648
Hou Y et al (2023) New insights into the critical role of inactive element substitution in improving the rate performance of sodium oxide cathode material. Energy Storage Mater 56:87–95
Liang X, Yu T-Y, Ryu H-H, Sun Y-K (2022) Hierarchical O3/P2 heterostructured cathode materials for advanced sodium-ion batteries. Energy Storage Mater 47:515–525
Jin J et al (2022) Unveiling the complementary manganese and oxygen redox chemistry for stabilizing the sodium-ion storage behaviors of layered oxide cathodes. Adv Funct Mater 32:2203424
Zhuang Z et al (2023) Ultrahigh-voltage LiCoO₂ at 4.7 V by interface stabilization and band structure modification. Adv Mater 35:2212059
Yu T-Y et al (2020) High-energy O3-Na_1-2xCa_x[Ni_0.5Mn_0.5]O₂ cathodes for long-life sodium-ion batteries. J Mater Chem A 8:13776–13786
Liang J et al (2023) A gradient oxy-thiophosphate-coated Ni-rich layered oxide cathode for stable all-solid-state Li-ion batteries. Nat Commun 14:146
Wang H et al (2023) In situ plastic-crystal-coated cathode toward high-performance Na-ion batteries. ACS Energy Lett 8:1434–1444
Xu GL et al (2022) Native lattice strain induced structural earthquake in sodium layered oxide cathodes. Nat Commun 13:436
Hong N et al (2024) Regulating phase transition and restraining Fe distortion at high potential window via rare earth metal incorporation on O3-type layered cathodes. Adv Funct Mater 34:2402398
Yu Y et al (2023) Triggering reversible anion redox chemistry in O3-type cathode through tuning Na/Mn anti-site defects. Energy Environ Sci 16:584–597
Joshi A et al (2023) High-entropy Co-free O3-type layered oxyfluoride: A promising air-stable cathode for sodium-ion batteries. Adv Mater 35:2304440
Li Y et al (2022) Interfacial engineering to achieve an energy density of over 200 Wh kg^– 1 in sodium batteries. Nat Energy 7:511–519
Zhang K et al (2023) Regulating phase transition and oxygen redox to achieve stable high-voltage O3-type cathode materials for sodium-ion batteries. Adv Energy Mater 13:2302793
Cheng Z et al (2022) A rational biphasic tailoring strategy enabling high-eerformance layered cathodes for sodium-ion batteries. Angew Chem Int Ed 61:202117728
Zhang Y et al (2020) Revisiting the Na_2/3Ni_1/3Mn_2/3O₂ cathode: oxygen redox chemistry and oxygen release suppression. ACS Cent Sci 6:232–240
Huang Y et al (2020) Vitalization of P2–Na_2/3Ni_1/3Mn_2/3O₂ at high-voltage cyclability via combined structural modulation for sodium-ion batteries. Energy Storage Mater 29:182–189
Lee SY et al (2024) Enhanced fast-discharging performance and cyclability in oxygen-redox-based P3-type Na-layered cathode via vacancies in TM layers. Adv Energy Mater, 2402412
Tang Y et al (2024) Sustainable layered cathode with suppressed phase transition for long-life sodium-ion batteries. Nat Sustain 7:348–359
Ryu H-H, Lim H-W, Lee SG, Sun Y-K (2024) Near-surface reconstruction in Ni-rich layered cathodes for high-performance lithium-ion batteries. Nat Energy 9:47–56
Oh S-M et al (2014) High capacity O3-type Na[Li_{0. 05}(Ni_{0. 25}Fe_{0. 25}Mn_{0. 5})_0.95]O₂ cathode for sodium ion batteries. Chem Mater 26:6165–6171
Niu YB et al (2020) High-efficiency cathode sodium compensation for sodium-ion batteries. Adv Mater 32:2001419
Zhang YY et al (2023) Refined electrolyte and interfacial chemistry toward realization of high-energy anode-free rechargeable sodium batteries. J Am Chem Soc 145:25643–25652
Ma M, Chen B, Tu Y, Pan H (2024) Ternary electrolyte enables high-voltage and high-temperature Na-ion batteries. ACS Energy Lett 9:4655–4665
Yu T-Y, Hwang J-Y, Bae IT, Jung H-G, Sun Y-K (2019) High-performance Ti-doped O3-type Na[Ti_x(Ni_0.6Co_0.2Mn_0.2)_1-x]O₂ cathodes for practical sodium-ion batteries. J Power Sources 422:1–8
Liang X, Kim H, Jung HG, Sun Y-K (2021) Lithium-substituted tunnel/spinel heterostructured cathode material for high-performance sodium-ion batteries. Adv Funct Mater 31:2008569
Liang X et al (2017) Surface modification of Na₃V₂(PO₄)₃ by nitrogen and sulfur dual-doped carbon layer with advanced sodium storage property. ACS Appl Mater Interfaces 9:13151–13162
Hwang J-Y et al (2016) Novel cathode materials for Na-ion batteries composed of spoke-like nanorods of Na[Ni_0.61Co_0.12Mn_0.27]O₂ assembled in spherical secondary particles. Adv Funct Mater 26:8083–8093
Li M et al (2024) Tailoring Cu-rich surface spinel phase for high-performance O3-type layered cathode naterials for sodium-ion batteries. Nano Energy 123:109375
Wang K et al (2022) Precipitate-stabilized surface enabling high-performance Na_0.67Ni_0.33-xMn_0.67Zn_xO₂ for sodium-ion battery. eScience 2:529–536
Ryu H-H et al (2021) Capacity fading mechanisms in Ni-rich single-crystal NCM cathodes. ACS Energy Lett 6:2726–2734

There is NO Competing Interest.

SupportingInformation.docx

Download PDF

Version 1

posted

You are reading this latest preprint version

High-energy and long-life O3-type layered cathode material for sodium-ion batteries

Status:

Version 1

Abstract

Figures

1 Introduction

2 Results

2.1 Formation of interface reconstruction layer

2.2 Na storage performance of surface-modified cathode

2.3 Structural evolution and reaction mechanism

3 Discussion

4 Methods

Declarations